Surface fatigue failure of analysis of two TIMKEN bearings

Failure analysis on bearing surface is an important link to improve TIMKEN bearings in reliability engineering (bearing lost its function in the work, thereby causing the failure, or does not work properly known as failure (bearing failure according to their failure and early failure of normal life can be divided into two kinds. This article is mainly directed against pitting corrosion and fatigue analysis of the causes leading to early failure of the bearing, and propose improvement measures to enhance the TIMKEN bearing service life and reliability.
Fatigue failure is one of the TIMKEN bearing surface failure mode, is the long-term effect of metal in the alternating load failure arising under, mainly for fatigue crack initiation and the propagation and fracture process. Cracks of two approaches:
First: from surface produced, that in TIMKEN bearing of contact process in the, due to outside contains of role in work surface caused cyclical changes of contact stress, in surface produced plastic deformation and deformation hardening, last in work surface appears tiny crack, by surface to in development, in the crack formed of two a surface Zhijian, due to lubricant of lobby doors wedged into, makes crack wall by force open, forced crack forward development;
Second: the crack from the surface, that is, under the effect of repeated stress in surface contact, crack first arose in some depth from the contact surface, and along with the surface at an angle of direction, once from the surface at a certain depth is reached, up to the surface and beyond, resulting pitting falling off, left a hemp pit on the contact surface.
Cracks arising in or from the surface from the surface, these two situations are existent (parts after surface carburizing, quenching heat treatment and so on, if the presence of uneven hardness is not uniform, as well as negative stress, such as, are under the effect of contact stress, cracks under normal from the surface. Conversely, if the poor quality of surface processing of parts, there is a defect (oxidation and decarburization), friction or poor lubrication, then cracked the surface.

Previous: Treatment methods of reducing the noise of NSK bearings
Next: From Visual inspection of INA bearing quality considerations

Hot Products:

Product Model	Inside Diameter	Outside Diameter	Thickness
23988CAE4 NSK	440	600	118
23284CAE4 NSK	420	760	272

【TradeBearings News Statement】

1.The news above mentioned with detailed source are from internet.We are trying our best to assure they are accurate ,timely and safe so as to let bearing users and sellers read more related info.However, it doesn't mean we agree with any point of view referred in above contents and we are not responsible for the authenticity. If you want to publish the news,please note the source and you will be legally responsible for the news published.
2.All news edited and translated by us are specially noted the source"TradeBearings".
3.For investors,please be cautious for all news.We don't bear any damage brought by late and inaccurate news.
4.If the news we published involves copyright of yours,just let us know.