INA Bearing erosion in three ways and impact on life

To predict the fatigue life of INA bearings, determine the remaining life of the bearing on the need to understand all the fatigue phenomenon, this will take a very long time. However, since the contact point of fatigue stress fatigue occurs, to achieve a great material damage will occur changes. Thus, in addition to the surface of incipient crack, roller suffer chemical effects, the crack propagation of the material before changing conditions, the test material change may determine the bearing fatigue.
INA bearings due to use of the environment is different, so the performance of erosion is different, because the erosion in different ways. Bearing this course, can not escape the fate of being eroded, following on to talk about the bearing being eroded in three ways.
1, cavitation
INA bearings cavitation is contact with the liquid and the solid surface for the relative motion of the surface damage arising form. When the low pressure lubricating oil film, the oil will form a bubble, the bubble movement to the high pressure zone, the bubbles collapse under pressure, at the moment of collapse have a great impact force and a high temperature, the solid surface in under repeated impact force, the material fatigue off, so that the friction surface of small pits, and then developed into a sponge-like scars. Overloading, high-speed, large changes in load and speed plain bearings, often cavitation;
2, the fluid erosion
INA Bearing fluid fluid erosion is intense shock to the solid surface can cause fluid erosion, the solid surface punctate scars, smooth surface of this damage;
3, the electrical erosion
Bearing corrosion is due to the electrical motor or electrical leakage, INA bearing friction between the surface of the spark, causing the friction surface on the point-like wounds, characterized in that the damage of the journal forth in hard surface.
INA Bearing fatigue, can be measured by using X-ray residual stress of the raceway surface of the diffraction line width at half amplitude, change in the amount of residual austenite to master.

Previous: Spherical bearings troubleshooting and inspection attention
Next: INA bearings and sealing grease selection

Hot Products:

Product Model	Inside Diameter	Outside Diameter	Thickness
7234ADB NSK	170	310	52
7034ADB NSK	170	260	42

【TradeBearings News Statement】

1.The news above mentioned with detailed source are from internet.We are trying our best to assure they are accurate ,timely and safe so as to let bearing users and sellers read more related info.However, it doesn't mean we agree with any point of view referred in above contents and we are not responsible for the authenticity. If you want to publish the news,please note the source and you will be legally responsible for the news published.
2.All news edited and translated by us are specially noted the source"TradeBearings".
3.For investors,please be cautious for all news.We don't bear any damage brought by late and inaccurate news.
4.If the news we published involves copyright of yours,just let us know.