Failure of the nine common bearings

1, the bearing temperature is too high: the operation of the institutions, the installation of the bearing parts are allowed a certain temperature is normal, should not feel hot when stroking institutions housing, otherwise the bearing temperature.
Bearing noise: Rolling work allows minor operation sound, if the noise is too large or unusual noise or crash, it indicates that the bearing failure.
3, the raceway surface metal peeling: the bearing rolling elements and the inner and outer ring raceway surface are exposed to periodic pulsating action of the load, thereby generating a periodic variation of contact stress. When after stress cycles reaches a certain value, the rolling element or the outer ring raceway work surface to produce fatigue spalling. If the bearing load is too large, will this fatigue exacerbated. In addition, the bearing installation errors, shaft bending, will produce the raceway flaking. Bearing raceway fatigue spalling will reduce the running accuracy of the shaft, the institutions vibration and noise.
4, the bearing burns: burn bearing its raceway, rolling element tempering color. Burn is generally insufficient lubrication, the quality of lubricating oil does not meet the requirements or deterioration, and tight bearing assembly.
5, plastic deformation: bearing raceway and roller contact surface appears uneven pits the bearing plastically deformed. The reason is that the bearings in large static loads or impact loads, the working surface of the local stress exceeds the yield limit of the material, which generally occurs in the low-speed rotation of the bearing.
Bearing race cracks: bearing race cracks may be bearing with tight, loose bearing foreign or inner ring bearing inclusive deformation, poor installation of the bearing surface processing.
7 holder fragmentation: The reason is insufficient lubrication, rolling body broken, such as seat skew.
8, the holder metal adhered on the rolling body, and the likely reason is that the rolling body is stuck within the holder or insufficient lubrication.
9 seat raceway severe wear: Block circle may fall into foreign body, lubricating oil or lubricating oil grades inappropriate.

Previous: Bearing troubleshooting method profiling
Next: The use of various types of bearings

Hot Products:

Product Model	Inside Diameter	Outside Diameter	Thickness
7956CTYNDBLP4 NSK	280	380	46
7952A5TYNDBLP4 NSK	260	360	46

【TradeBearings News Statement】

1.The news above mentioned with detailed source are from internet.We are trying our best to assure they are accurate ,timely and safe so as to let bearing users and sellers read more related info.However, it doesn't mean we agree with any point of view referred in above contents and we are not responsible for the authenticity. If you want to publish the news,please note the source and you will be legally responsible for the news published.
2.All news edited and translated by us are specially noted the source"TradeBearings".
3.For investors,please be cautious for all news.We don't bear any damage brought by late and inaccurate news.
4.If the news we published involves copyright of yours,just let us know.