Bearing fatigue damage types

Bearing fatigue damage in two ways, the most important one is the most bearing parts appear spalling pits (pitting), the depth and direction of the rolling contact surfaces on the measured width of the same order of magnitude. Pitting forming in load, the metal particles crack mouth edge appears, and a scrolling direction along pitting expanding trend bearings can not use the result. Standard bearing life calculation must first determine the situation does appear to operate until the damaged work deadlines.
The second form is surface spalling. Shallow depth peeling, usually only a few microns, or less than 1μm (some literature called up to 20μm). Usually in the bearings running tens of millions of turn or turn into segments after peeling. Such peeling type into segments in most cases will not damage the general purpose (ie, no special requirements) of the bearing, while the high-precision and high-speed bearings, it is not allowed to come off the above into segments.

Previous: How to reduce the temperature and vibration effects on bearing life
Next: Analytical techniques bearing friction torque

Hot Products:

Product Model	Inside Diameter	Outside Diameter	Thickness
7322ADB NSK	110	240	50
7222CDB NSK	110	200	38

【TradeBearings News Statement】

1.The news above mentioned with detailed source are from internet.We are trying our best to assure they are accurate ,timely and safe so as to let bearing users and sellers read more related info.However, it doesn't mean we agree with any point of view referred in above contents and we are not responsible for the authenticity. If you want to publish the news,please note the source and you will be legally responsible for the news published.
2.All news edited and translated by us are specially noted the source"TradeBearings".
3.For investors,please be cautious for all news.We don't bear any damage brought by late and inaccurate news.
4.If the news we published involves copyright of yours,just let us know.